HSS T5 steel | 1.3265 | HS18-0-2-9 | SKH4 | W18Cr4V2Co8 | UNS T52005 | 2756
Reference standard: ASTM A600, DIN 17350, EN ISO 4957, JIS G 4805, GB/T 9943, SS14
AISI/ SAE T5 Steel is Tungsten type containing cobalt high speed steel, red hardness and high temperature hardness and wearability Than T4/ W18Cr4VCo5 steel is high, but the toughness is low, after quenching, surface hardness is 64-64 HRC. Used as materials in more than 400 hb hardness under complex conditions (heavy duty) work of turning tool, milling cutter, cutter, etc.
Download Full Datasheet
Chemical composition of SAE T5 HSS steel AISI High Speed Steel
| ASTM A681 | C | Si | Mn | P | S | Cr | Mo | V | W | Co |
| T5 / T52005 | 0.75～0.85 | 0.20～0.40 | 0.20～0.40 | 0.030 Max | 0.030 Max | 3.75～5.00 | 0.50～1.25 | 1.80～2.40 | 17.5～19.0 | 7.00～9.50 |
| DIN 17350 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
| 1.3265 / HS18-0-2-9 | 0.72～0.80 | ≤0.45 | ≤0.40 | 0.030 Max | 0.030 Max | 3.80～4.50 | 0.50～0.80 | 1.40～1.70 | 17.5～18.50 | 9.00～10.00 |
| JIS G4805 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
| SKH4 | 0.73～0.83 | ≤0.45 | ≤0.40 | 0.030 Max | 0.030 Max | 3.80～4.50 | 0.50-1.20 | 1.00～1.50 | 17.00～19.00 | 9.00～11.00 |
| SS14 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
| 2756 | 0.70～0.85 | 0.15～0.30 | 0.20～0.40 | 0.030 Max | 0.030 Max | 4.00～5.00 | 0.80～1.20 | 1.30～0.90 | 17.5～19.5 | 9.50～11.5 |
| GB/T 9943 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
| W18Cr4V2Co8 | 0.75～0.85 | 0.20～0.40 | 0.20～0.40 | 0.030 Max | 0.030 Max | 3.75～5.00 | 0.50～1.25 | 1.80～2.40 | 17.50～19.00 | 7.00～9.50 |
SAE T5 steel equivalent –HSS steel grade
- AISI ASTM SAE T5 in USA HSS Steel material standard
- SS14 2756 in Swedish Steel material standard
- JIS SKH4- Japanese High Speed Steel Grade Standard
- DIN HS18-0-2-9 HSS steel grade material
- W-Nr 1.3265 HSS
Form of Supply
ASTM ASI – SAE T5 high speed tool steel, we can supply the round bar, flat bar, plate, hexagonal and square block. Diameters can be sawn to your required lengths as one offs or multiple cut pieces. Rectangular pieces can be sawn from flat bar or plate to your specific sizes. Ground tool steel bar and precision ground steel plate can be supplied, providing a quality precision finished bar to tight tolerances.
Applications
As a high quality HSS tool steel ASTM AISI – SAE T5 is very suitable for make complex blanking, high speed Drill bar, vibration and impact load of the mold: deep drawing die, punching die. Metal cutting saw blades, cold heading and extrusion tools. It have very good hot hardness.
Supply Range of SAE AISI T5 tool Steel
- T5steel round bar: diameter 20mm to 1400mm
- T5 steel plate: Thickness 20mm to 1400mm
Others have not specified size, pls contact our experienced sales team.
Forging of HSS T5 Tool steel-ASTM A681
Slowly Heat to 816-871 °C, Then rapid heating to 1200°C.keep the temperature to heat thoroughly. Start forging. Finished cool slowly. Below 850 °C no forging process.
Annealing of SAE AISI T5 tool steel material
Heat to 850 -910°C, soak enough time, and ensure heat thoroughly. Then cool in the heat treatment furnace. After Annealing get Hardness 285 HRc Max.
Quenching of SAE T5 material
Preheat temperature /°C: 816 ~ 816
Quenching temperature /°C| salt bath furnace: 1277
Quenching temperature / °C | controlled atmosphere furnace: 1288
Tempering of T5 steel grade material
Tempering temperature /°C: 550 ~ 550
After tempering hardness HRC or higher: 63
More T5 tool steel heat treatment data, please contact your heat treatment supplier.
Processing
We Provide the sawing cutting, Milled, polishing and make drill bar, Etc.
If you have any inquiry and problems, Please don’t hesitate to discuss with us.