ASTM-AISI | SAE Middle HSS M52 tool steel (UNS T11350)
Reference standard: ASTM A600, DIN 17350, EN ISO 4957, JIS G 4805, GB/T 9943, SS14
SAE M52 Steel is a American Middle high speed Steel grade standard, it have lower alloy composition, so its price is lower a lot than others standard high speed steel material. We supply M52 HSS in round bar, flat bar, sheet, plate, square, block, etc.
Chemical composition of SAE M52 HSS steel ASTM A600 High Speed Steel
| ASTM A681 | C | Si | Mn | P | S | Cr | Mo | V | W |
| M52/ T11350 | 0.85~0.95 | 0.20～0.60 | 0.15～0.45 | 0.030 Max | 0.030 Max | 3.50～4.30 | 4.00~4.90 | 1.65～2.25 | 0.75～1.50 |
| DIN 17350 | C | Si | Mn | P | S | Cr | Mo | V | w |
| / | / | ||||||||
| GB/T 9943 | C | Si | Mn | P | S | Cr | Mo | V | w |
| / | / | ||||||||
| JIS G4403 | C | Si | Mn | P | S | Cr | Mo | V | w |
| / | / |
SAE M52 steel equivalent –HSS steel grade
- AISI ASTM SAE M52 in USA HSS Steel material standard
- GB have not similar grade in Chinese Steel material standard
- JIS have not equivalent material grade- Japanese High Speed Steel
- DIN HSS steel grade material
- W-Nr HSS
- Swedish SS14
Form of Supply
ASTM ASI – SAE M52 high speed tool steel, we can supply the round bar, flat bar, plate, hexagonal and square block. Diameters can be sawn to your required lengths as one offs or multiple cut pieces. Rectangular pieces can be sawn from flat bar or plate to your specific sizes. Ground tool steel bar and precision ground steel plate can be supplied, providing a quality precision finished bar to tight tolerances.
Applications
As a high quality HSS tool steel ASTM AISI – SAE M52 is very suitable for make complex blanking, high speed Drill bar, vibration and impact load of the mold: deep drawing die, punching die. Metal cutting saw blades, cold heading and extrusion tools.
Supply Range of SAE AISI M52 tool Steel
- M52 steel round bar: diameter 20mm to 1400mm
- M52 steel plate: Thickness 20mm to 1400mm
Others have not specified size, please contact our experienced sales team.
Forging of HSS M52 Tool steel-ASTM A681
Slowly Heat to 650-750 °C, keep the temperature to heat thoroughly. Start forging. Finished cool slowly.
Annealing of SAE AISI M52 tool steel material
Heat to 1204 °C, soak enough time, and ensure heat thoroughly. Then cool in the heat treatment furnace. Get hardness 248 HRc Max.
Quenching of SAE M52 material
Preheat temperature/ ℃: 732 ~ 843
Quenching temperature / ℃ | salt bath furnace: 1163
Quenching temperature / ℃ | controlled atmosphere furnace: 1174
Tempering of M52 steel grade material
Heat uniformly at the tempering temperature for M52 tool steel material. Keep enough time, then cool in air
Advice temperature 538 °C. After tempering get 63 HRc Min. More M52 tool steel heat treatment data, please contact your heat treatment supplier,.
We Provide the sawing cutting, Milled, polishing and make drill bar, Etc.